Shell Polymers 65N8U
Technology
Gas Phase
Melt index
8.2
Density
0.965
Comonomer
Homo
Details
Shell Polymers HDPE 65N8U is a homopolymer that provides excellent stiffness, low warpage, and easy processability. This grade is ideal for the production of cases, crates, totes, bins, and other articles requiring high stiffness.
Highlights
- Excellent stiffness
- Low warpage
- High top load
- Gas Phase technology
Additives
None
| Property Value | Method | Nominal Value (Eng) | Nominal Value (Si) |
|---|---|---|---|
| Environmental Stress-Cracking Resistance (ESCR)(a) | ASTM D1693 | 3 hr | 3 hr |
| Tensile(b) Strength at Yield | ASTM D638 | 4640 psi | 32.0 MPa |
| Tensile(b) Strength at Break | ASTM D638 | 2000 psi | 13.8 MPa |
| Tensile(b) Elongation at Yield | ASTM D638 | 7.30% | 7.30% |
| Tensile(b) Elongation at Break | ASTM D638 | 225% | 225% |
| Flexural Modulus 1% Secant | ASTM D790B | 252,400 psi | 1740 MPa |
| Flexural Modulus 2% Secant | ASTM D790B | 213,200 psi | 1470 MPa |
| Tensile Impact Strength | ASTM D1822 | 21.4 ft.lb/in2 | 45.0 kj/m2 |
| Notched Izod Impact(-30°C) | ASTM D256 | 0.88 ft.lb/in | 47.0 J/m |
Breaking down technical data sheets
Interpreting a technical data sheet (TDS) can sometimes feel like deciphering hieroglyphics—which is why we created a handy guide that breaks down what to look for.
Download guide (PDF, 573 kB)
Interested to learn more?
From technical properties to applications and more, our team is happy to answer any questions you might have.
Connect with an expert